    图5.1是不同VOx负载量的xVCe8Zr2催化剂的XRD谱图。从图5.1中可以看出,2θ值为28.8°、33.3°、47.9°和56.8°处的衍射峰为立方萤石晶相的CeO2特征峰,与CeO2的衍射卡片JCPDS (81-0792)相一致,没有ZrO2的特征峰出现,说明Zr离子已经进入CeO2的晶格中形...[继续阅读]

    用共沉淀法制备了不同Cr/V比的Cr-V-O复合氧化物催化剂。图4.1为Cr-V-O催化剂的XRD谱图。图4.1 催化剂的XRD谱图:基线为CrVO4,*-Cr2O3,V-V2O5,-Cr2V4O13Fig.4.1 XRD patterns of catalysts: baseline- CrVO4,*-Cr2O3,V-V2O5,-Cr2V4O13由图可知,随着V的加入,催化剂中除了...[继续阅读]

    [1]X Gao,Q Xin,X Guo. Appl. Catal. A,1994,114: 197.[2]C Watling,G Deo,K Seshan,et al. Catal. Today,1996,28: 139.[3]T Blasco,A Galli,J M López-Nieto,et al. J. Catal.,1997,169: 203.[4]Argyle M D,Chen K,Bell A T,et al. J. Catal.,2002,208: 139.[5] Liu Y M,Fen...[继续阅读]

    稀土钒酸盐材料由于其独特的d电子和f电子结构、大的原子磁矩和很强的自旋轨道效应等特性,具有比单一的钒氧化物材料有更好的活性和奇特的光学、电学和磁学等性能。由于其较高的热稳定性和较强的储氧及释氧能力(OSC),作为催...[继续阅读]

    为了详细研究催化剂的表面组成,以及表面阳离子和阴离子的化学状态,对8VCe2Zr8和8VCe8Zr2催化剂进行了XPS表征分析。图5.12a为0 1s的精细XPS谱。从图5.12a中可以看出两个催化剂的0 1s在结合能为531.2eV和529.5eV处各有一峰,这表明催化剂表面...[继续阅读]

    复合氧化物催化剂物理化学性能除了取决于制备方法等外界因素外,最根本的因素是其构成元素的原子结构。丙烷在不同气氛下脱氢是一个复杂的物理化学过程,涉及固体催化剂和各原料气体的相互作用,如果能建立起催化剂的原子结...[继续阅读]

    观察方程(6.9)模型参数系数,讨论各个参数对转化率的影响,δ2的系数为负,它们对转化率的贡献是负的,(△X)2、Z/R、△n2/3、T、2×(e/a)2/3和常数项的系数为正,它们对转化率的贡献是正的。丙烷氧化脱氢反应涉及电子得失的过程,电负性差...[继续阅读]

    纳米CeVO4材料的制备:称取0.8mmolCe(NO3)3·6H2O溶于20mL去离子水中,加入一定量的EDTA,继续搅拌0.5h后,缓慢加入2M的NaOH水溶液直至溶液澄清,称取0.8mmolNH4VO3加入溶液中,继续搅拌0.5h至溶液变亮黄色,用2M的NaOH水溶液调pH值达到10,将溶液移至反应...[继续阅读]

    不同方法制备的3CrZr催化剂上丙烷氧化脱氢反应在固定床微分反应器中进行,C3H8:O2为1:1,总流速50ml/min,气相色谱在线分析反应产物。反应主要产物为C3H6和深度氧化产物CO和CO2,没有检测到裂解产物C2H6、C2H4和CH4。图3.17为三种催化剂上丙...[继续阅读]